Wähle ein anderes Land oder eine andere Region, um Inhalte für deinen Standort zu sehen.Select another country or region to see content for your location.Seleccione otro país o región para ver el contenido de su ubicación.Selecteer een ander land of een andere regio om de inhoud van uw locatie te zien.Vælg et andet land eller område for at se indhold, der er specifikt for din placering.Voit katsoa paikallista sisältöä valitsemalla jonkin toisen maan tai alueen.Choisissez un pays ou une région pour afficher le contenu spécifique à votre emplacement géographique.Επίλεξε μια άλλη χώρα ή περιοχή, για να δεις περιεχόμενο σχετικό με την.Scegli il Paese o territorio in cui sei per vedere i contenuti locali.別の国または地域を選択して、あなたの場所のコンテンツを表示してください。Velg et annet land eller region for å se innhold som gjelder der.Escolha para ver conteúdos específicos noutro país ou região.Välj ett annat land eller område för att se det innehåll som finns där.Konumunuza özel içerikleri görmek yapmak için başka bir ülkeyi veya bölgeyi seçin.Chọn quốc gia hoặc khu vực khác để xem nội dung cho địa điểm của bạn
A high-performance dry-lubricant film which is anchored fast due to the chemical reaction with the surface of the MoS2 lubricant film. The product is used for treating iron and steel (not high-alloy steel). LM 51 is made up of two components which are mixed together before use.
A high-performance dry-lubricant film which is anchored fast due to the chemical reaction with the surface of the MoS2 lubricant film. The product is used for treating iron and steel (not high-alloy steel). LM 51 is made up of two components which are mixed together before use.
Used as a pre-treatment for difficult cold-form processes. Used for the manufacture of lead-in layers in bearings, pistons, screws and nuts etc.
Application
LM 51 is made up of two components which are mixed together shortly before use.
Mixing ratio 82 parts by weight of Component I to 18 parts by weight of Component II This corresponds to 75 parts by volume of Component I to 10 parts by volume of Component II
Before mixing, Component I must be stirred. The mixture must also be stirred at regular intervals to make sure that the MoS2 is uniformly distributed in the mixture.
The mixture when ready should not be stored for more than 5 days.
Before application, the components must be clean, free from grease and dry. LM 51 can be applied by immersion, spraying or brush.
The coating thicknesses depend on the treatment time and the treatment temperature. For immersion, the treatment time should be between 5 and 20 minutes at a treatment temperature of around 60 °C. LM 51 can also be used at room temperature. In this case, the immersion time should be 30 minutes. Thinner coats can also be produced.
For spray coatings, it is advisable to apply several thin coats.
After the film has dried, a thin film of LM 48 Spray Paste or a corrosion inhibitor oil such as LCP 55 can be applied for long-term protection.